Tensile Behavior of Carbon Fiber-Reinforced Polymer Composites Incorporating Nanomaterials after Exposure to Elevated Temperature
Table 2
Tensile test results of the CFRP test specimens.
| Specimens | Mechanical parameters | 1 (GPa) | SD2 | (MPa) | SD | | SD | Toughness (MPa·mm/mm) | SD |
| CFRP | 53.34 | 4.30 | 492.32 | 12.45 | 0.0144 | 0.00082 | 3.60 | 0.28 | MWCNT-CFRP | 41.55 | 2.32 | 528.69 | 6.42 | 0.0174 | 0.00068 | 4.59 | 0.22 | GnPs-CFRP | 41.87 | 5.89 | 490.31 | 36.32 | 0.0164 | 0.00027 | 4.02 | 0.36 | S-MWCNT-COOH-CFRP | 44.98 | 8.40 | 604.35 | 55.95 | 0.0212 | 0.00027 | 6.40 | 0.66 | S-MWCNT-COOH-CFRP-T50 | 42.54 | 5.71 | 502.17 | 40.92 | 0.0190 | 0.00155 | 4.80 | 0.72 | S-MWCNT-COOH-CFRP-T100 | 47.74 | 7.22 | 383.87 | 32.86 | 0.0133 | 0.00091 | 2.56 | 0.32 | S-MWCNT-COOH-CFRP-T150 | 50.43 | 8.74 | 417.77 | 39.54 | 0.0144 | 0.00067 | 3.02 | 0.39 | S-MWCNT-COOH-CFRP-T200 | 44.77 | 10.30 | 403.18 | 13.03 | 0.0130 | 0.00087 | 2.62 | 0.16 |
|
|
1Initial stiffness (or elastic modulus) at 30% of the peak strength in the ascending branch. 2Standard deviation.
|