Quantitative Phase-Field Simulation of Composition Partition and Separation Kinetics of Nanoscale Phase in Fe-Cr-Al Alloy

<div>The average interparticle distance <svg height="12.5612pt" id="M184" style="vertical-align:-3.27287pt" version="1.1" viewbox="-0.0498162 -9.28833 15.8491 12.5612" width="15.8491pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M530 686C535 705 530 712 521 712C504 712 448 684 359 674L358 648H393C437 648 439 646 429 593L400 435C372 447 345 448 332 448C286 448 194 414 144 373C68 311 23 203 23 111C23 26 57 -12 91 -12C120 -12 147 3 188 29C227 54 290 102 341 170H343L322 71C308 6 320 -12 341 -12C373 -12 442 27 501 96L485 120C455 91 422 67 408 67C401 67 401 76 404 91C440 294 479 473 530 686ZM387 375L355 241C326 187 200 53 142 53C126 53 109 73 109 130C109 217 154 337 218 381C240 396 265 404 297 404S372 390 387 375Z"></path></g><g transform="matrix(.0091,0,0,-0.0091,7.15,3.132)"><path d="M433 39L423 65C413 59 399 54 387 54C370 54 352 69 352 114V299C352 352 342 392 307 422C285 440 255 449 225 449C168 437 102 399 75 379C56 365 44 353 44 339C44 315 69 296 87 296C101 296 111 303 116 319C124 349 133 371 145 385C156 397 171 404 190 404C241 404 275 364 275 291V274C253 256 180 229 120 209C65 190 39 159 39 110C39 47 88 -12 159 -12C189 -12 237 25 277 52C282 35 288 21 301 8C312 -3 333 -12 348 -12L433 39ZM275 84C256 65 221 48 195 48C164 48 124 73 124 124C124 161 146 180 185 198C206 208 254 229 275 240V84Z"></path></g><g transform="matrix(.0091,0,0,-0.0091,10.98,3.132)"><path d="M478 437H300V411C357 404 363 393 347 345C325 280 293 190 258 107C229 178 188 284 163 354C147 397 149 405 203 411V437H-2V411C52 403 59 396 82 339C130 222 176 109 220 -11H248C304 138 356 261 390 336C417 395 425 404 478 411V437Z"></path></g></svg> of the <svg height="11.6425pt" id="M185" style="vertical-align:-0.2063999pt" version="1.1" viewbox="-0.0498162 -11.4361 11.3068 11.6425" width="11.3068pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M545 106L524 126C493 85 467 65 455 65C438 65 427 113 405 238C448 295 498 362 543 439L533 448L478 435C453 386 423 331 398 295H395C370 404 347 448 282 448C169 448 23 309 23 153C23 54 65 -12 128 -12C203 -12 283 70 339 155H341C360 29 380 -12 411 -12C444 -12 491 11 545 106ZM333 204C265 95 210 54 169 54C137 54 113 96 113 171C113 302 191 405 252 405C301 405 318 306 333 204Z"></path></g><g transform="matrix(.0091,0,0,-0.0091,7.385,-5.741)"><path d="M310 541L304 571C290 586 211 619 185 610L80 76L131 52L310 541Z"></path></g></svg> phase in the Fe-38 at.% Cr-10 at.% Al alloy as a function of time when aged at 720, 740, and 760 K.</div>

Journal of Nanomaterials

fig6

Figure 6

Figure 6: Quantitative Phase-Field Simulation of Composition Partition and Separation Kinetics of Nanoscale Phase in Fe-Cr-Al Alloy 