Quantitative Phase-Field Simulation of Composition Partition and Separation Kinetics of Nanoscale Phase in Fe-Cr-Al Alloy

Table 1

Composition variations of the α phase for the different aging temperatures and times.

(K)		α composition (at.%)
		Fe	Cr	Al
720	0.5	51.92	38.07	10.01	1.00
	282	41.79	50.59	7.62	1.45
	322	20.37	76.49	3.14	3.87
	402	7.49	91.66	0.85	17.36
	1982	6.90	92.30	0.80	18.88
740	0.5	51.97	38.03	10.00	1.00
	102	38.94	54.06	7.00	1.54
	122	10.69	87.79	1.52	8.36
	142	8.48	90.48	1.04	13.97
	1982	8.16	90.87	0.97	14.83
760	0.5	51.96	38.05	9.99	1.00
	42	40.41	52.25	7.34	1.50
	62	9.85	88.89	1.26	11.44
	1982	9.50	89.27	1.23	11.76