Research Article
Characterization of Pr-Doped LaF3 Nanoparticles Synthesized by Different Variations of Coprecipitation Method
Table 4
The values of the size (
) of the NPs treated by MW irradiation in different crystallography orientations.
| Peak (hkl)/ (nm) | 1 : 1 SLNPs | 1 : 1 SLNPs (30 min MW) | 1 : 1 SLNPs (90 min MW) | 1 : 1 SLNPs (180 min MW) |
| (002) | 14.8 | 15.8 | 16.1 | 19.7 | (110) | 16.4 | 17.2 | 17.4 | 19.7 | (111) | 16.0 | 16.3 | 16.8 | 18.4 | (112) | 13.6 | 16.0 | 16.6 | 18.5 | (300) | 14.3 | 14.5 | 15.7 | 16.6 | (113) | 13.7 | 14.2 | 14.9 | 16.4 | (302) | 12.7 | 12.8 | 13.7 | 13.8 | (221) | 15.9 | 15.6 | 16.0 | 19.0 | (223) | 12.9 | 13.2 | 13.9 | 14.9 | (115) | 12.7 | 13.2 | 13.9 | 14.8 | Mean | 14.2 | 14.9 | 15.5 | 17.2 | Standard deviation | 1.3 | 1.5 | 1.3 | 1.8 |
|
|