Electrospun High-Thermal-Resistant Inorganic Composite Nonwoven as Lithium-Ion Battery Separator
Figure 2
Photographs in (a)–(d) sequentially correspond to the SEM image of the PVDF-HFP surface of SPF after heat treatment at 150°C, 160°C, 170°C, and 180°C for 20 min. Photographs in (e)–(h) sequentially correspond to the SEM image of the SiO2 surface of SPF after heat treatment at 150°C, 160°C, 170°C, and 180°C for 20 min. Photographs in (e)–(l) show the cross-section SEM of the composite separator after heat treatment at 150°C, 160°C, 170°C, and 180°C for 20 min.