Towards Sophisticated 3D Interphase Modelling of Advanced Bionanocomposites via Atomic Force Microscopy
Table 1
Modelling parameters used for PVA bionanocomposite films.
| Modelling parameter | PVA/HNT | PVA/Cloisite 30B clay | Ref. |
| (GPa) | 2.08 | 2.08 | [45] | (GPa) | 140a | 178b | a[46] b[32] | (nm) | 208 (3 wt% HNTs) | 109 (3 wt% Cloisite 30B) | [45] | 410 (5 wt% HNTs) | 206 (5 wt% Cloisite 30B) | [45] | 900.6 (10 wt% HNTs) | 560 (10 wt% Cloisite 30B) | [45] | (nm) | | 4.6 (3 wt% Cloisite 30B) | [45] | | 15.8 (5 wt% Cloisite 30B) | [45] | | 41.6 (10 wt% Cloisite 30B) | [45] | (nm) | 35.2 (3 wt% HNTs) | | [45] | 66.5 (5 wt% HNTs) | | [45] | 85 (10 wt% HNTs) | | [45] | (g cm-3) | 0.39 | 0.39 | [45] | (g cm-3) | 1.8 | 1.98 | Material data sheets | (nm) | ~7.3 | ~10.4 | [45] | (nm) | 10 | 10 | [32] | | 0.4 | 0.4 | [34] | | | 0.66 | [32] | (nm) | | 1.87 | [45] | (nm) | | 3.6 | [45] | | | 5.6 | [45] | (nm) | | 0.98 | [45] | (g cm-3) | | 3.1 | [45] | (m2 g-1) | 40.3c | 658d | c[47] d[32] |
|
|