Microwave Synthesis of MCM-41 and Its Application in CO2 Absorption by Nanofluids
Table 1
Properties of MCM-41 synthesized at different microwave conditions.
| Sample | Different parameters | a (m2g-1) | b (cm3g-1) | (nm) | (Å) | (Å) | (Å) | Factor | Value |
| WH-t0 | Microwave time (min) | 0 | 518.1 | 0.663 | 3.027 | 37.77 | 43.61 | — | WH-t5 | 5 | 1158.3 | 1.069 | 3.815 | 38.11 | 44.01 | 7.77 | WH-t15 | 15 | 1210.3 | 1.224 | 3.825 | 38.41 | 44.35 | 8.01 | WH-t30 | 30 | 1115.6 | 1.088 | 3.821 | 38.75 | 44.74 | 8.44 | WH-t60 | 60 | 1102.0 | 1.149 | 3.815 | 39.26 | 45.33 | 9.09 | WH-t90 | | 90 | 1095.1 | 1.199 | 3.824 | 39.26 | 45.33 | 9.00 | WH-t120 | | 120 | 1053.5 | 1.146 | 3.815 | 38.92 | 44.94 | 8.70 |
| WH-T80 | Microwave temperature (°C) | 80 | 1164.7 | 0.976 | 3.820 | 38.99 | 45.02 | 8.73 | WH-T90 | 90 | 1180.1 | 0.991 | 3.823 | 38.61 | 44.58 | 8.26 | WH-T100 | 100 | 1210.3 | 1.224 | 3.825 | 38.41 | 44.35 | 8.01 | WH-T110 | 110 | 1200.3 | 1.214 | 3.824 | 37.55 | 43.36 | 7.03 | WH-T120 | 120 | 903.3 | 0.939 | 3.813 | 36.72 | 42.40 | 6.18 |
| WH-P50 | Microwave power (W) | 50 | 928.1 | 0.954 | 3.806 | 39.00 | 45.03 | 8.87 | WH-P100 | 100 | 997.1 | 0.942 | 3.812 | 39.16 | 45.22 | 9.01 | WH-P150 | 150 | 1188.4 | 1.195 | 3.821 | 38.76 | 44.76 | 8.46 | WH-P200 | 200 | 1210.3 | 1.224 | 3.825 | 38.41 | 44.35 | 8.01 | WH-P250 | 250 | 1182.3 | 1.222 | 3.814 | 37.55 | 43.36 | 7.13 | WH-P300 | 300 | 937.2 | 0.960 | 3.805 | 36.58 | 42.34 | 6.19 |
|
|
aBET method. b-plot method. cMean pore width was determined using the BJH method. |