Microstructural Study of Hydration of C<sub>3</sub>S in the Presence of Calcium Nitrate Using Scanning Transmission X-Ray Microscopy (STXM)

<table class="table-group" id="tab1"><tr><td><table class="table"><tr><td class="thead-hr" colspan="7"><hr/></td></tr><tr><td class="align_left">Sample</td><td class="align_center">C<sub>3</sub>S 3 d</td><td class="align_center">C<sub>3</sub>S 7 d</td><td class="align_center">C<sub>3</sub>S 28 d</td><td class="align_center">CN 3 d</td><td class="align_center">CN 7 d</td><td class="align_center">CN 28 d</td></tr><tr><td class="align_left">BET area</td><td class="align_center">9.16</td><td class="align_center">11.29</td><td class="align_center">33.52</td><td class="align_center">15.89</td><td class="align_center">25.95</td><td class="align_center">38.52</td></tr><tr><td class="align_left">Langmuir area</td><td class="align_center">12.92</td><td class="align_center">16.26</td><td class="align_center">47.19</td><td class="align_center">22.88</td><td class="align_center">37.59</td><td class="align_center">54.71</td></tr><tr class="table-tr"><td colspan="7"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

<div>Specific surface area of C<sub>3</sub>S pastes with different hydration times (m<sup>2</sup>/g).</div>

Journal of Nanomaterials

tab1

Table 1

Table 1: Microstructural Study of Hydration of C<sub>3</sub>S in the Presence of Calcium Nitrate Using Scanning Transmission X-Ray Microscopy (STXM) 

Journal of Nanomaterials

Microstructural Study of Hydration of C3S in the Presence of Calcium Nitrate Using Scanning Transmission X-Ray Microscopy (STXM)

Table 1

Microstructural Study of Hydration of C₃S in the Presence of Calcium Nitrate Using Scanning Transmission X-Ray Microscopy (STXM)