Enhancement of Mechanical Properties on Novel Friction Stir Welded Al-Mg-Zn Alloy Joints Reinforced with Nano-SiC Particles
Table 2
Mechanical properties of fabricated samples with joint efficiency.
| Sample composition | Ultimate tensile strength (MPa) | Hardness (HV) | Yield strength (MPa) | Joint efficiency (%) |
| Al-Mg-Zn/1.0 wt% nano-SiC | 125 | 137 | 94 | 0.43 | Al-Mg-Zn/1.5 wt% nano-SiC | 143 | 152 | 99 | 0.50 | Al-Mg-Zn/2.0 wt% nano-SiC | 157 | 163 | 107 | 0.55 | Al-Mg-Zn/2.5 wt% nano-SiC | 178 | 167 | 133 | 0.62 | Al-Mg-Zn/3 wt% nano-SiC | 191 | 171 | 165 | 0.67 |
|
|