Evaluation of Prestrain Annealing Impact on Nanomaterial Sensitization
Table 4
Characterization of the MAO-coated ZK60 Mg alloy and the bare ZK60 Mg alloy [
45].
| Sample | Roughness average (μm) | Mean pore diameter (μm) | Area percent of pores (% of total) | The thickness of the coating (μm) |
| Substrate | 0.089 | — | — | — | Dc | | | | | 250 V | 0.190 | 0.82 | 5.54 | 4.8 | Unipolar pulsed | | | | | 250 V | 0.570 | 2.03 | 47.8 | 5.5 | 300 V | 1.439 | 4.15 | 36.9 | 9.8 | 350 V | 2.456 | 11.2 | 18.6 | 19.6 | 400 V | 3.441 | 13.4 | 14.2 | 22.1 | Bipolar pulsed | | | | | 250 V-20 V | 0.193 | 0.48 | 28.5 | 5.5 | 300 V-20 V | 1.950 | 3.73 | 18.3 | 13.2 | 350 V-20 V | 2.844 | 11.5 | 9.77 | 23.5 | 400 V-20 V | 3.017 | 7.42 | 5.94 | 24.3 |
|
|