Recent Progress on Carbon Nanomaterials for Resisting the Wear Damages
Table 1
Tribological performances of CNTs-reinforced composite coatings.
| Matrixes | Additives | Conditions | Contents | Friction coefficients, wear (mm3/Nm) |
| Mg-1Al [92] | Fullerene | 48 mm/s, 20 N | 0.5 wt% | ∼0.4, ∼0.015 | 96 mm/s, 20 N | ∼0.385, ∼0.017 | Epoxy [118] | C70 | 4 N | 1 wt% | ∼0.234, ∼0.0126 | 3 wt% | ∼0.168, ∼0.0024 | Al 7075 [101] | CNTs | 450 (rpm), 20 N | 0.75 p | 8.8 μm/min | 450 (rpm), 60 N | 15.2 μm/min | Al [119] | MWCNT | 0.12 m/s, 30 N | 4.5 vol% | 0.042, ∼36.6 | Epoxy [118] | MWCNTs | 4 N | 1 wt% | ∼0.171, ∼0.092 | 3 wt% | ∼0.188, ∼0.032 | CuO [120] | Graphene | 1.1 GPa | | ∼0.09, ∼0.0287 | 2.0 GPa | | ∼0.10, ∼0.0528 | Epoxy [73] | NDs | 1,000 m, 10 N | 0.25 wt% | ∼0.38, ∼0.516 | 0.75 wt% | ∼0.22, ∼0.352 | Ti [121] | NDs | 200 N | 0.1 wt% | Wear ∼0.89% | 0.5 wt% | Wear ∼0.41% |
|
|