Influence of Nanoclay Filler Material on the Tensile, Flexural, Impact, and Morphological Characteristics of Jute/E-Glass Fiber-Reinforced Polyester-Based Hybrid Composites: Experimental, Modeling, and Optimization Study

Table 8

Results of the flexural test.

Specimen designation	Jute (wt.%)	E-glass (wt.%)	wt.% of Cloisite 20 nanoclay (wt. %)	Flexural strength (MPa)	Flexural modulus (MPa)
S1	10	10	2	74.89	117.56
S2	10	20	4	76.52	119.65
S3	10	30	6	79.56	121.89
S4	15	10	4	78.36	123.56
S5	15	20	6	80.56	124.89
S6	15	30	2	82.45	126.59
S7	20	10	6	83.21	127.31
S8	20	20	2	85.15	275.15
S9	20	30	4	90.22	261.33