Fabrication and Experimental Estimation of Mechanical Properties of Kevlar-Glass/Epoxy Interwoven Composite Laminate
| Orientation | Gauge length L = 4 × b (mm) | Breadth (b) (mm) | Thickness (t) (mm) | Load (P) (N) | Flexural strength (F = 3PL/2bt2) (MPa) | Average flexural strength (MPa) |
| 1 × 1 | 55.2 | 13.8 | 3.2 | 1,390 | 814.45 | 905.68 | 55.2 | 13.4 | 2.8 | 1,310 | 1,032.48 | 56 | 14.1 | 3.1 | 1,430 | 886.49 | 56.4 | 14 | 3.2 | 1,380 | 814.37 | 55.8 | 13.6 | 2.9 | 1,340 | 980.61 |
| 3 × 3 | 56 | 14 | 3.3 | 1,480 | 815.43 | 860.86 | 55.2 | 13.8 | 3.2 | 1,410 | 826.17 | 54 | 13.5 | 3.1 | 1,390 | 867.85 | 55.7 | 14.2 | 2.9 | 1,430 | 1,000.46 | 56.3 | 13.6 | 3.2 | 1,310 | 794.39 |
| 5 × 5 | 52.8 | 13.2 | 3.2 | 1,440 | 843.75 | 859.79 | 55.6 | 13.9 | 3.1 | 1,310 | 817.90 | 54.8 | 13.7 | 3 | 1,390 | 926.67 | 55.3 | 14.3 | 3.3 | 1,410 | 751.05 | 53.8 | 13.6 | 2.9 | 1,360 | 959.57 |
|
|