Fabrication and Experimental Estimation of Mechanical Properties of Kevlar-Glass/Epoxy Interwoven Composite Laminate
Table 5
Compression test results.
| Orientation | Cross sectional length (l) (mm) | Cross sectional breadth (b) (mm) | Cross sectional area (A) (l × b) (mm2) | Load (P) (N) | Compressive strength (c = P/A) (MPa) | Average compressive strength (MPa) |
| 1 × 1 | 3 | 14 | 42 | 6,170 | 146.90 | 136.05 | 3.3 | 13.8 | 45.54 | 6,250 | 137.24 | 3.5 | 13.6 | 47.6 | 6,530 | 137.18 | 3.7 | 14.1 | 52.17 | 6,380 | 122.29 | 3.6 | 13.4 | 48.24 | 6,590 | 136.61 |
| 3 × 3 | 3.4 | 14.4 | 48.96 | 6,380 | 130.31 | 122.54 | 3.7 | 13.9 | 51.43 | 6,050 | 117.64 | 3.6 | 13.7 | 49.32 | 6,010 | 121.86 | 3.5 | 14.1 | 49.35 | 6,140 | 124.42 | 3.7 | 14.3 | 52.91 | 6,270 | 118.50 |
| 5 × 5 | 3.7 | 13.8 | 51.06 | 6,280 | 122.99 | 123.94 | 3.5 | 13.7 | 47.95 | 6,580 | 137.23 | 3.7 | 13.9 | 51.43 | 6,110 | 118.80 | 3.9 | 14.1 | 54.99 | 6,370 | 115.84 | 3.7 | 13.4 | 49.58 | 6,190 | 124.85 |
|
|