Fabrication of Electrospun Polyamide-6/Chitosan Nanofibrous Membrane toward Anionic Dyes Removal
Table 3
Full factorial central composite design for removal of Solophenyl Red 3BL and Polar Yellow GN.
| Run no. | Solution PH (A) | Initial dye concentration (B) | Electrospinning time (C) | Chitosan ratio (D) | (%) removal (Solophenyl Red 3BL) | (%) removal (Polar Yellow GN) | Exp. | Predicted | Exp. | Predicted |
| 1 | 5 | 50 | 2 | 10 | 68 | 69.67 | 72 | 70.83 | 2 | 9 | 50 | 2 | 10 | 61 | 61.5 | 56 | 54.83 | 3 | 5 | 100 | 2 | 10 | 71 | 69.33 | 79 | 80.08 | 4 | 9 | 100 | 2 | 10 | 64 | 61.16 | 61 | 64.08 | 5 | 5 | 50 | 4 | 10 | 75 | 79.33 | 83 | 85.75 | 6 | 9 | 50 | 4 | 10 | 68 | 71.17 | 69 | 69.75 | 7 | 5 | 100 | 4 | 10 | 76 | 78.99 | 97 | 95 | 8 | 9 | 100 | 4 | 10 | 67 | 70.83 | 78 | 79 | 9 | 5 | 50 | 2 | 30 | 83 | 86.67 | 84 | 84.5 | 10 | 9 | 50 | 2 | 30 | 58 | 57.49 | 61 | 59.5 | 11 | 5 | 100 | 2 | 30 | 88 | 86.33 | 86 | 85.25 | 12 | 9 | 100 | 2 | 30 | 59 | 57.17 | 62 | 60.25 | 13 | 5 | 50 | 4 | 30 | 97 | 96.33 | 95 | 93.91 | 14 | 9 | 50 | 4 | 30 | 69 | 67.17 | 71 | 68.92 | 15 | 5 | 100 | 4 | 30 | 98 | 95.99 | 98 | 94.67 | 16 | 9 | 100 | 4 | 30 | 66 | 66.83 | 66 | 69.67 | 17 | 3 | 75 | 3 | 20 | 92 | 89.83 | 97 | 98.75 | 18 | 11 | 75 | 3 | 20 | 52 | 52.5 | 59 | 57.75 | 19 | 7 | 25 | 3 | 20 | 85 | 80.83 | 64 | 65.25 | 20 | 7 | 125 | 3 | 20 | 78 | 80.17 | 76 | 75.25 | 21 | 7 | 75 | 1 | 20 | 57 | 61.5 | 64 | 64.58 | 22 | 7 | 75 | 5 | 20 | 83 | 80.83 | 89 | 88.92 | 23 | 7 | 75 | 3 | 0 | 74 | 64.67 | 79 | 76.58 | 24 | 7 | 75 | 3 | 40 | 79 | 77.67 | 78 | 80.92 | 25 | 7 | 75 | 3 | 20 | 72 | 77.67 | 64 | 66 | 26 | 7 | 75 | 3 | 20 | 69 | 77.67 | 68 | 66 | 27 | 7 | 75 | 3 | 20 | 73 | 77.67 | 66 | 66 | 28 | 7 | 75 | 3 | 20 | 71 | 77.67 | 65 | 66 | 29 | 7 | 75 | 3 | 20 | 70 | 77.67 | 67 | 66 | 30 | 7 | 75 | 3 | 20 | 68 | 77.67 | 66 | 66 |
|
|