Bifunctional Tailoring of Platinum Surfaces with Earth Abundant Iron Oxide Nanowires for Boosted Formic Acid Electro-Oxidation
Figure 1
CVs measured in 0.5 M H2SO4 at a scan rate 100 mV·s−1 at bare curve A and nonactivated curve B and activated curve C (at −0.5 V), curve D (at −0.9 V), and curve E (at −1.3 V) nano-FeOx-modified Pt (a), Au (b), and GC (c) substrates. Activation was pursued for 10 min in 0.2 mole·L−1 NaOH.