Assessment of Ruthenium Dye N719 Adsorption Kinetics in Mesoporous TiO₂ Films of Dye-Sensitized Solar Cells via Nanoplasmonic Sensing

Table 1

Short-circuit current density, open-circuit voltage, and efficiency of devices fabricated with (a) 3 μm and (b) 10 μm mesoporous TiO₂ films using dyes N3, N749, Z907, and N719.

	Isc (mA/cm^2)	Voc (V)	Efficiency (%)
(a) 3 μm
N3	2.667	0.553	1.10
N749	3.642	0.602	1.66
Z907	6.940	0.687	3.72
N719	1.934	0.609	0.95
(b) 10 μm
N3	2.250	0.523	0.91
N749	5.996	0.600	2.65
Z907	9.727	0.667	4.62
N719	6.833	0.672	3.25