Research Article
Electrochemical Analysis of Architecturally Enhanced LiFe0.5Mn0.5PO4 Multiwalled Carbon Nanotube Composite
Figure 5
The cyclic voltammograms of composite LiFe0.5Mn0.5PO4-MWCNTs (a) and LiFe0.5Mn0.5PO4 (b) in 1 M LiPF6 containing 1 : 1 v/v ethylene carbonate–dimethyl carbonate solvent mixture between 0.1 and 0.8 mV/s. (c) Voltage range: 0.0–0.80 V and comparative Nyquist plots: (i) LiFe0.5Mn0.5PO4-MWCNTs and (ii) LiFe0.5Mn0.5PO4 at formal potential of 0.71 V vs. Li/Li+ and perturbation amplitude of 10 mV.
(a) |
(b) |
(c) |