Influence of Zn/Fe Molar Ratio on Optical and Magnetic Properties of ZnO and ZnFe<sub>2</sub>O<sub>4</sub> Nanocrystal as Calcined Products of Layered Double Hydroxides

<table>Kubelka-Munk transformed reflectance spectra of (a) reflectance spectra of ZnO/ZnFe<sub>2</sub>O<sub>4</sub> nanocomposite, (b) band-gap energy of ZnO, (c) Kubelka-Munk plot ZnO/ZnFe<sub>2</sub>O<sub>4</sub> nanocomposite (for sample Z3F as an example), and (d) diffuse reflectance UV-visible absorption spectra of calcined Zn-Fe-LDH nanostructure.</table>

Journal of Spectroscopy

fig3

Figure 3

Figure 3: Influence of Zn/Fe Molar Ratio on Optical and Magnetic Properties of ZnO and ZnFe<sub>2</sub>O<sub>4</sub> Nanocrystal as Calcined Products of Layered Double Hydroxides 

Figure 3 | Influence of Zn/Fe Molar Ratio on Optical and Magnetic Properties of ZnO and ZnFe2O4 Nanocrystal as Calcined Products of Layered Double Hydroxides 