Research Article
Evaluation of Temper Embrittlement of 30Cr2MoV Rotor Steels Using Electrochemical Impedance Spectroscopy Technique
Table 3
FATT50-related parameters.
| Sample | Measured FATT50 | Impedance () | P (%) | C (%) | Mn (%) | S (%) | Reduction (%) |
Predicted value | Difference |
| A31 | −70.9 | 0.07 | 0.019 | 0.24 | 0.62 | 0.001 | 72.2 | −73.432 | −2.532 | A32 | −54.1 | 0.09 | 0.019 | 0.24 | 0.62 | 0.001 | 71.33 | −48.674 | 5.426 | 411 | 67.5 | 0.1 | 0.045 | 0.28 | 0.66 | 0.013 | 64.47 | 70.87 | 3.37 | A21 | 82 | 0.09 | 0.065 | 0.28 | 0.68 | 0.012 | 60.3 | 94.862 | 12.862 | 412 | 95.6 | 0.12 | 0.045 | 0.28 | 0.66 | 0.013 | 62.33 | 94.866 | −0.734 | 431 | 103.6 | 0.11 | 0.063 | 0.28 | 0.69 | 0.014 | 56.57 | 112.3 | 8.7 | A22 | 127.1 | 0.11 | 0.065 | 0.28 | 0.68 | 0.012 | 52.57 |
115.504 | −11.596 | 432 | 142.2 | 0.13 | 0.063 | 0.28 | 0.69 | 0.014 | 55.33 | 136.836 | −5.364 | 421 | 198.7 | 0.11 | 0.107 | 0.3 | 0.69 | 0.014 | 52.8 | 199.99 | 1.29 | 422 | 211.7 | 0.12 | 0.107 | 0.3 | 0.69 | 0.014 | 54.17 | 213.452 | 1.752 | 441 | 235 | 0.13 | 0.204 | 0.3 | 0.69 | 0.015 | 46.65 | 229.632 | −5.368 | 442 | 275.4 | 0.18 | 0.204 | 0.3 | 0.69 | 0.015 | 30.5 | 283.142 | 7.742 |
|
|