Enamel Based Composite Layers Deposited on Titanium Substrate with Antifungal Activity
Table 1
The main functional IR groups present in the structure of Ti-Enamel and Ti-PDMS-Enamel layers.
| Wavenumber (cm−1) | IR bands assignment | Ti-Enamel | Ti-PDMS-Enamel |
| 491, 590, 640, 685 | Vibrations in ions | Vibrations in ions | 750 | Si-O/Si-CH3 vibrational group [34, 35] | Si-O/Si-CH3 vibrational group [34, 35] | 796 | — | Si-O vibrations in SiO4 groups | 817 | — | Si-O-Si bonds [36] | 832 | Si-O stretching vibrations | — | 860 | — | Si-CH3 rocking vibration [36] | 890 | Vibrations in ions | Vibrations in ions | 951 | Symmetric P-O stretching mode | — | 964 | — | Si-OH vibrational group | 1014, 1090 | — | Si-O-Si vibrations [36] | 1042, 1052, 1063, 1094 | Asymmetric P-O stretching mode | Asymmetric P-O stretching mode | 1130, 1179, 1216 | Vibrations in ions | Vibrations in ions | 1260 | — | CH3 vibrations in Si-CH3 group [36] | 1387, 1408, 1425, 1441 | Vibrations in ions [35] | Vibrations in ions [37] |
|
|