Silver Chloride Encapsulation-Induced Modifications of Raman Modes of Metallicity-Sorted Semiconducting Single-Walled Carbon Nanotubes

Table 1

The peak positions (RS) and relative area intensity (I) of the individual components of the RBM-band of Raman spectra of the pristine and AgCl-filled SWCNTs as well as diameters of the corresponding nanotubes. Asterisks denote the peaks in the spectra of the filled SWCNTs that are the same as in the spectra of the pristine SWCNTs.

λex (nm)	SWCNT			AgCl@SWCNT
	Component of RBM-band		Tube diameter, nm	Component of RBM-band		Tube diameter, nm
	RS	I		RS	I
458	171	0.36	1.4	166	0.30	1.4
	178	0.64	1.3	177^∗	0.61	1.3
				190	0.09	1.2
488	169	0.78	1.4	159	0.23	1.5
	184	0.22	1.3	168^∗	0.35	1.4
				180	0.33	1.3
				190	0.09	1.2
514	157	0.08	1.5	153	0.16	1.6
	168	0.20	1.4	168^∗	0.36	1.4
	178	0.38	1.3	179^∗	0.05	1.3
	184	0.27	1.3	184^∗	0.43	1.3
	189	0.07	1.2
531	159	0.11	1.5	157^∗	0.14	1.5
	172	0.31	1.4	168^∗	0.22	1.4
	178	0.30	1.3	181^∗	0.16	1.3
	185	0.21	1.3	187^∗	0.48	1.3
	191	0.07	1.2
568	161	0.14	1.5	156	0.20	1.6
	168	0.31	1.4	167^∗	0.37	1.4
	176	0.55	1.4	175^∗	0.36	1.4
				186	0.07	1.3