Silver Chloride Encapsulation-Induced Modifications of Raman Modes of Metallicity-Sorted Semiconducting Single-Walled Carbon Nanotubes

Table 2

The peak positions (RS) and relative area intensity (I) of the components of the G-band (G_E2g, G_TO, and G_LO) of Raman spectra of the pristine and AgCl-filled SWCNTs. The shifts of the components of the filled SWCNTs relative to the position of the pristine nanotubes are given in parentheses.

λex (nm)	Sample	Component of G-band (cm^−1)
		GE2g		GTO		GLO
		RS	I	RS	I	RS	I
458	SWCNT	1556	0.08	1569	0.12	1596	0.80
	AgCl@SWCNT	1558 (+2)	0.10	1574 (+5)	0.12	1602 (+6)	0.78
488	SWCNT	1559	0.10	1572	0.11	1598	0.79
	AgCl@SWCNT	1561 (+2)	0.14	1576 (+4)	0.11	1603 (+5)	0.75
514	SWCNT	1556	0.11	1569	0.11	1595	0.78
	AgCl@SWCNT	1556	0.11	1572 (+3)	0.13	1602 (+7)	0.76
531	SWCNT	1557	0.11	1570	0.10	1594	0.79
	AgCl@SWCNT	1553 (−4)	0.04	1574 (+4)	0.20	1604 (+10)	0.76
568	SWCNT	1558	0.10	1572	0.09	1595	0.81
	AgCl@SWCNT	1555 (−3)	0.09	1577 (+5)	0.17	1603 (+8)	0.74