Solution of the Nonlinear High-Fidelity Generalized Method of Cells Micromechanics Relations via Order-Reduction Techniques

Table 1

Fiber and matrix constituent properties.

	T (°C)	E (MPa)	ν	σy (MPa)	CTE (με/°C)
Fiber	-	74000	0.20	-	4.9
Matrix	−25	2100	0.36	54.0	158.0
	0	1400	0.36	43.9	158.0
	23	950	0.36	28.0	158.0
	50	480	0.36	18.0	158.0