Mathematical Problems in Engineering / 2019 / Article / Fig 10

Research Article

Recrystallization Microstructure Prediction of a Hot-Rolled AZ31 Magnesium Alloy Sheet by Using the Cellular Automata Method

Figure 10

Rolled microstructures in the biting zone of the AZ31 magnesium alloy: (a) rolling sketch image; (b) six roller warm rolling mill; (c) microstructure of the deformation zone; (d) coarse twin grains in the A zone via EBSD experimental observation; (e) coarse grains after extrusion crushing in the B zone via EBSD experimental observation; (f) coarse grains after extrusion crushing in the C zone via EBSD experimental observation; (g) recrystallizedfine grains in the D zone via EBSD experimental observation; (h) simulated initial grains using the CA method; (i) simulated recrystallized fine grains using the CA method.

We are committed to sharing findings related to COVID-19 as quickly and safely as possible. Any author submitting a COVID-19 paper should notify us at help@hindawi.com to ensure their research is fast-tracked and made available on a preprint server as soon as possible. We will be providing unlimited waivers of publication charges for accepted articles related to COVID-19. Sign up here as a reviewer to help fast-track new submissions.