Material details of the base plate and stiffeners (data are summarized from [
38–
41]).
| | Chemical element | Content (%) |
| | Carbon (C) | 0.42–0.50 | | Iron (Fe) | 98.51–98.98 | | Manganese (Mn) | 0.60–0.90 | | Phosphorous (P) | ≤0.040 | | Sulfur (S) | ≤0.050 |
| | Mechanical property | Metric |
| | Density (kg/mm3) | 7.87 × 10−6 | | Young’s modulus (MPa) | 200000 | | Poisson’s ratio | 0.29 | | Yield strength (MPa) | 310 | | Ultimate tensile strength (MPa) | 565 | | Shear modulus (MPa) | 80000 | | Bulk modulus (MPa) | 140000 | | Elongation at break (in 50 mm-%) | 16.0 | | Reduction of area (%) | 40.0 | | Hardness (Brinell) | 163 | | Hardness (Rockwell B) | 84 |
|
|