Mathematical Modeling of Multiple Quality Characteristics of a Laser Microdrilling Process Used in Al7075/SiCp Metal Matrix Composite Using Genetic Programming Table 3 Comparison between experimental and predicted values of HAZ at R 2 = 99.88.
No. PP (W) ( ) PF (Hz) ( ) AGP (kg/cm2 ) ( ) PW (ms) ( ) HAZ (mm) Error % Experimental GP 1 240 230 8 0.4 0.04 4.19E − 02 −0.00188 2 230 210 10 0.5 0.112 0.107232 0.004768 3 230 230 12 0.3 0.068 7.13E − 02 −0.00328 4 210 230 10 0.3 0.068 7.17E − 02 −0.00368 5 220 240 12 0.2 0.081 8.02E − 02 0.000789 6 240 220 12 0.3 0.078 7.82E − 02 −0.00023 7 220 210 9 0.4 0.088 8.75E − 02 0.000453 8 250 220 8 0.6 0.104 0.103178 0.000822 9 210 210 8 0.2 0.065 6.80E − 02 −0.00305 10 250 210 12 0.4 0.1 9.97E − 02 0.000311 11 210 230 10 0.4 0.069 7.04E − 02 −0.00139 12 240 220 12 0.4 0.073 7.20E − 02 0.00103 13 230 220 11 0.6 0.085 8.46E − 02 0.000417 14 220 250 8 0.3 0.102 0.101978 2.21E − 05 15 220 230 11 0.6 0.089 8.67E − 02 0.002272 16 220 220 10 0.5 0.094 9.50E − 02 −0.00098 17 240 240 9 0.6 0.105 0.102995 0.002005 18 240 210 11 0.2 0.085 8.12E − 02 0.003847 19 220 250 8 0.2 0.0747 7.28E − 02 0.001893 20 230 250 9 0.5 0.1 0.103908 −0.00391 21 210 220 9 0.3 0.082 8.05E − 02 0.001512 22 210 250 12 0.5 0.0909 9.14E − 02 −0.00051 23 210 250 12 0.6 0.0921 9.28E − 02 −0.00071 24 220 210 9 0.3 0.101 0.101721 −0.00072 25 240 240 9 0.5 0.1 0.10225 −0.00225 26 230 250 9 0.4 0.094 9.11E − 02 0.002885 27 240 250 10 0.6 0.096 9.56E − 02 0.000406 28 250 210 12 0.5 0.097 9.83E − 02 −0.00131 29 230 230 12 0.2 0.076 7.74E − 02 −0.0014 30 220 230 11 0.5 0.092 9.06E − 02 0.001379 31 210 240 11 0.4 0.072 7.25E − 02 −0.00049 32 230 210 10 0.6 0.095 9.25E − 02 0.002548 33 250 250 11 0.3 0.078 7.72E − 02 0.000826 34 250 220 8 0.5 0.105 0.104177 0.000823 35 210 220 9 0.2 0.084 7.68E − 02 0.007168 36 220 240 12 0.6 0.095 9.20E − 02 0.003025 37 230 240 8 0.4 0.055 4.67E − 02 0.008281 38 210 210 8 0.6 0.1 9.79E − 02 0.002054 39 250 230 9 0.2 0.07 7.45E − 02 −0.00448 40 240 250 10 0.2 0.095 8.29E − 02 0.012098 41 240 210 11 0.3 0.08 7.90E − 02 0.001025 42 230 240 8 0.3 0.09 8.87E − 02 0.001309 43 210 240 11 0.5 0.084 9.04E − 02 −0.00638 44 250 240 10 0.3 0.065 7.74E − 02 −0.01241 45 250 230 9 0.6 0.095 9.90E − 02 −0.00402 46 250 250 11 0.4 0.08 0.081854 −0.00185 47 230 220 11 0.2 0.077 0.0783 −0.0013 48 220 220 10 0.4 0.075 0.07292 0.00208 49 250 240 10 0.2 0.091 8.82E − 02 0.002776 50 240 230 8 0.5 0.09 0.090104 −0.0001