Modelling and Simulation in Engineering / 2019 / Article / Tab 4 / Research Article
Mathematical Modeling of Multiple Quality Characteristics of a Laser Microdrilling Process Used in Al7075/SiCp Metal Matrix Composite Using Genetic Programming Table 4 Comparison between experimental and predicted values of taper at R 2 = 99.43.
No. PP (W) ( ) PF (Hz) ( ) AGP (kg/cm2 ) ( ) PW (ms) ( ) Taper (deg) Error % Experimental GP 1 230 250 9 0.4 3.5 3.48E + 00 0.020539 2 230 240 8 0.4 3.702 3.68349 0.01851 3 210 220 9 0.3 3.815 3.816499 −0.0015 4 230 210 10 0.5 3.75 3.72E + 00 0.034738 5 240 250 10 0.2 4.135 4.12E + 00 0.017045 6 210 240 11 0.4 3.45 3.43E + 00 0.023249 7 230 230 12 0.3 3.925 3.86E + 00 0.064339 8 220 240 12 0.6 3.5 3.487621 0.012379 9 220 240 12 0.2 4.12 4.13E + 00 −0.00979 10 240 220 12 0.3 3.8 3.81E + 00 −0.00709 11 230 240 8 0.3 3.8 3.79E + 00 0.010771 12 220 250 8 0.3 3.962 3.96E + 00 0.006659 13 230 220 11 0.2 4.16 4.16E + 00 −0.00037 14 240 220 12 0.4 3.775 3.757363 0.017637 15 250 230 9 0.6 3.8 3.770205 0.029795 16 210 210 8 0.6 4.2 4.200192 −0.00019 17 230 220 11 0.6 3.75 3.718309 0.031691 18 220 250 8 0.2 4.05 4.10E + 00 −0.04831 19 250 210 12 0.4 4.1 3.96E + 00 0.138649 20 250 220 8 0.5 3.5 3.522696 −0.0227 21 240 240 9 0.5 3.4 3.41E + 00 −0.01021 22 210 210 8 0.2 4.1 4.10E + 00 0.00162 23 240 230 8 0.5 3.505 3.523799 −0.0188 24 210 230 10 0.4 3.58 3.633331 −0.05333 25 220 210 9 0.3 3.6 3.774172 −0.17417 26 250 250 11 0.3 3.8 3.846722 −0.04672 27 210 240 11 0.5 3.307 3.441274 −0.13427 28 250 240 10 0.2 4.1 4.105488 −0.00549 29 220 230 11 0.5 3.3 3.441037 −0.14104 30 240 250 10 0.6 3.8 3.81E + 00 −0.00654 31 230 210 10 0.6 3.305 3.638603 −0.3336 32 230 250 9 0.5 3.38 3.41E + 00 −0.03093 33 230 230 12 0.2 4.05 4.110147 −0.06015 34 210 220 9 0.2 4 4.125376 −0.12538 35 250 230 9 0.2 4.15 4.123817 0.026183 36 240 240 9 0.6 3.75 3.748872 0.001128 37 240 210 11 0.3 3.9 3.86E + 00 0.043294 38 250 210 12 0.5 3.65 3.501807 0.148193 39 210 250 12 0.6 3.25 3.47E + 00 −0.21634 40 210 250 12 0.5 3.45 3.49592 −0.04592 41 220 220 10 0.5 3.6 3.572536 0.027464 42 240 210 11 0.2 3.95 4.11E + 00 −0.16276 43 250 220 8 0.6 3.6 4.114297 −0.5143 44 220 220 10 0.4 3.8 3.694675 0.105325 45 250 250 11 0.4 3.9 3.655343 0.244657 46 240 230 8 0.4 3.6 3.615975 −0.01597 47 220 230 11 0.6 3.4 3.677536 −0.27754 48 220 210 9 0.4 3.5 3.48E + 00 0.023193 49 250 240 10 0.3 3.8 3.80E + 00 0.004566 50 230 250 9 0.4 3.5 3.48E + 00 0.020539