Stress Corrosion Cracking Behavior of TP 439 and 690 TT under Film-Forming Amine Environment
Figure 10
High temperature SSRT test fracture of 690 TT alloy under argon.
(a) Overview |
(b) Central area |
(c) Marginal zone |
(d) Marginal zone |