Stress Corrosion Cracking Behavior of TP 439 and 690 TT under Film-Forming Amine Environment
Table 2
The mechanical properties obtained from the SSRT test.
| Material | Environment | Temperature /°C | Maximum tensile strength /MPa | Elongation rate /% | Rate of reduction in area /% | Absorption area before fracture | Sensitivity index |
| TP 439 | FA | 260 | 388 | 21.9 | 48.6 | 91 | 6% | TP 439 | Non-FA | 260 | 388 | 11.4 | 53.6 | 89 | 8% | TP 439 | Argon | 260 | 412 | 27.1 | 89.1 | 97 | / | 690 TT | FA | 284 | 570 | 45.4 | 70.6 | 245 | 9% | 690 TT | Non-FA | 284 | 568 | 39.0 | 68.8 | 242 | 11% | 690 TT | Argon | 284 | 661 | 45.4 | 53.8 | 272 | / |
|
|
The stress corrosion sensitivity index is calculated based on the fracture absorption energy. |