Study on the Phase Equilibria of the Fe-Al-Ni-O System at 750°C
Table 3
Constitution of the corundum and matrix phases coexisting in the Fe-Al-Ni-O system at 750°C.
| No. | Substrate | Oxides | Al | Fe | Ni | Matrix phases | O | Al | Fe | Ni | Oxide phases |
| A1 | 10.8 | 86.9 | 2.3 | α | 58.4 | 36.5 | 1.4 | 3.7 | Corundum | A2 | 10.7 | 85.2 | 4.1 | α | 59.9 | 36.2 | 1.5 | 2.4 | Corundum | 37.8 | 41.0 | 21.2 | β | | | | | | A3 | 8.9 | 85.2 | 5.9 | α | 60.6 | 35.8 | 1.7 | 1.9 | Corundum | 32.3 | 30.2 | 37.5 | β | | | | | | 8.6 | 76.1 | 15.3 | γ | | | | | | A4 | 31.3 | 30.8 | 37.9 | β | 56.7 | 36.9 | 2.3 | 4.1 | Corundum | 8.4 | 66.4 | 25.2 | γ | | | | | | A5 | 7.6 | 54.9 | 37.5 | γ | 57.9 | 36.4 | 2.2 | 3.5 | Corundum | A6 | 5.7 | 49.5 | 44.8 | γ | 59.5 | 37.1 | 0.3 | 3.1 | Corundum | A7 | 4.1 | 35.1 | 60.8 | γ | 56.2 | 37.0 | 1.4 | 5.4 | Corundum | A8 | 3.7 | 17.4 | 78.9 | γ | 61.2 | 35.0 | 0.3 | 3.5 | Corundum |
|
|