Processing of Aluminium-Silicon Alloy with Metal Carbide as Reinforcement through Powder-Based Additive Manufacturing: A Critical Study
Table 3
Optimized conditions for aluminium-based (matrix) and MC (reinforcement) [
31,
58,
66,
89–
102].
| ES | MAM-P | M-R | LP (W) | SS (mm/s) | LT (μm) | HS (μm) | BT (°C) |
| Laser | SLM | AlSi10Mg-3% TiC | 80-140 | 200 | 50 | 50 | 100 | Laser | SLM | AlSi10Mg-5% TiC | 100 | 100-400 | 50 | 50 | — | Laser | SLM | AlSi15-5% TiC | 360 | 650 | 20 | 100 | — | Laser | DED | AlSi10Mg-5% TiC | 3000 | 10 | — | 2000 | — | Laser | DED | AlSi10Mg-30 Vol% TiC | 1800 | 7-17 | — | — | 100-200 | Laser | SLM | Al9.8Si0.6MgTi- TiC | 400 | — | — | 90 | — | Laser | SLM | AlSi10Mg-5% TiC | 320 | 1100 | 30 | 130 | — | Laser | SLM | AlSi10Mg-15% SiC | 500 | 600-2100 | 40 | 60-180 | — | Laser | SLM | AlSi10Mg-5 Vol% SiC | 195 | 640-880 | 30 | 500 | — | Laser | SLM | AlSi10Mg-10 Vol% SiC | 195 | 640-880 | 30 | 500 | — | Laser | SLM | Al-15% SiC | 500 | — | 50 | 100 | — | Laser | Laser sintering | Al–7Si–0.3Mg—5 to 12 Vol % SiC | 8.6 | — | 100 | 30 | 80 | Laser | SLM | AlSi10Mg-20% SiC | 200 | 100 | 30 | 50 | — | Laser | SLM | Al7Si-10 Vol% SiC | 200 | 500-1750 | 50 | 100 | — | Laser | SLM | AlSi10Mg-20% B4C | 100-200 | 100 | 50 | 130 to 150 | — |
|
|
ES: energy source; MAM-P: metal-based additive manufacturing; M-R: matrix-reinforcement; LP: laser power; SS: scanning speed; LT: layer thickness; HS: hatch spacing; BT: bed temperature.
|