Volume 2016, Article ID 5852328, 6 pages
http://dx.doi.org/10.1155/2016/5852328
Research Article

Development of a Composite Technique for Preconditioning of 41Cr4 Steel Used as Gear Material: Examination of Its Microstructural Characteristics and Properties

1College of Material Science and Engineering, Chongqing University of Technology, Chongqing 400054, China
2Chongqing Municipal Key Laboratory of Institutions of Higher Education for Mould Technology, Chongqing 400054, China
3Faculty of Materials and Energy, Southwest University, Chongqing 400715, China

Received 22 May 2016; Revised 23 July 2016; Accepted 10 August 2016

Academic Editor: Parashuram Sahoo

Copyright © 2016 Jianjun Hu et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Linked References

  1. R. K. Pandey, “Failure analysis of coal pulveriser gear box,” Engineering Failure Analysis, vol. 14, no. 4, pp. 541–547, 2007. View at Publisher · View at Google Scholar · View at Scopus
  2. H. C. Kim, “Sector gear and gas-insulated switchgear having the same,” Patent US20130167675, 2013.
  3. G. Meschut, O. Hahn, D. Teutenberg, and L. Ernstberger, “Influence of the dosing and mixing technology on the property profile of two-component adhesives,” Welding in the World, vol. 59, no. 1, pp. 91–96, 2015. View at Publisher · View at Google Scholar · View at Scopus
  4. V. Ngo, T. Hofman, M. Steinbuch, and A. Serrarens, “Effect of gear shift and engine start losses on energy management strategies for hybrid electric vehicles,” International Journal of Powertrains, vol. 4, no. 2, pp. 141–162, 2015. View at Google Scholar
  5. X. Nie, “Study of the rapid surface modification technology,” Heat Treatment of Metals, no. 3, pp. 19–22, 1997. View at Google Scholar
  6. M. Tarakci, K. Korkmaz, Y. Gencer, and M. Usta, “Plasma electrolytic surface carburizing and hardening of pure iron,” Surface & Coatings Technology, vol. 199, no. 2-3, pp. 205–212, 2005. View at Publisher · View at Google Scholar · View at Scopus
  7. Z. J. Tian, L. I. Jie, D. J. Shen, and Y. L. Wang, “Liquid phase plasma electrolytic carburizing, nitriding, carbonitriding technique,” Electroplating & Finishing, vol. 25, no. 2, pp. 53–56, 2006. View at Google Scholar
  8. C. Tsotsos, A. L. Yerokhin, A. D. Wilson, A. Leyland, and A. Matthews, “Tribological evaluation of AISI 304 stainless steel duplex treated by plasma electrolytic nitrocarburising and diamond-like carbon coating,” Wear, vol. 253, no. 9-10, pp. 986–993, 2002. View at Publisher · View at Google Scholar · View at Scopus
  9. A. L. Yerokhin, A. Leyland, C. Tsotsos, A. D. Wilson, X. Nie, and A. Matthews, “Duplex surface treatments combining plasma electrolytic nitrocarburising and plasma-immersion ion-assisted deposition,” Surface & Coatings Technology, vol. 142–144, no. 7, pp. 1129–1136, 2001. View at Publisher · View at Google Scholar · View at Scopus
  10. D. Wu, J. Zhang, J. C. Huang, H. Bei, and T. G. Nieh, “Grain-boundary strengthening in nanocrystalline chromium and the Hall-Petch coefficient of body-centered cubic metals,” Scripta Materialia, vol. 68, no. 2, pp. 118–121, 2013. View at Publisher · View at Google Scholar · View at Scopus
  11. D. B. Bober, M. Kumar, and T. J. Rupert, “Nanocrystalline grain boundary engineering: increasing Σ3 boundary fraction in pure Ni with thermomechanical treatments,” Acta Materialia, vol. 86, pp. 43–54, 2015. View at Publisher · View at Google Scholar
  12. X. Bin-Shi, W. Hai-Dou, D. Shi-Yun, and J. Bin, “Fretting wear-resistance of Ni-base electro-brush plating coating reinforced by nano-alumina grains,” Materials Letters, vol. 60, no. 5, pp. 710–713, 2006. View at Publisher · View at Google Scholar · View at Scopus
  13. B. Wu, B.-S. Xu, B. Zhang, X.-D. Jing, and C.-L. Liu, “Automatic brush plating: an update on brush plating,” Materials Letters, vol. 60, no. 13-14, pp. 1673–1677, 2006. View at Publisher · View at Google Scholar · View at Scopus
  14. B. Subramanian, S. Mohan, and S. Jayakrishnan, “Structural, microstructural and corrosion properties of brush plated copper-tin alloy coatings,” Surface and Coatings Technology, vol. 201, no. 3-4, pp. 1145–1151, 2006. View at Publisher · View at Google Scholar · View at Scopus
  15. Y. D. Gamburg and G. Zangari, Theory and Practice of Metal Electrodeposition, Springer, New York, NY, USA, 2011.
  16. N. Guo, Q. Liu, Y. C. Xin, B. F. Luan, and Z. Zhou, “The application of back-scattered electron imaging for characterization of pearlitic steels,” Science China Technological Sciences, vol. 54, no. 9, pp. 2368–2372, 2011. View at Publisher · View at Google Scholar · View at Scopus
  17. J. Zou, T. Grosdidier, K. Zhang, and C. Dong, “Mechanisms of nanostructure and metastable phase formations in the surface melted layers of a HCPEB-treated D2 steel,” Acta Materialia, vol. 54, no. 20, pp. 5409–5419, 2006. View at Publisher · View at Google Scholar · View at Scopus
  18. J. J. Hu, G. B. Zhang, H. B. Xu, and Y. F. Chen, “Microstructure characteristics and properties of 40Cr steel treated by high current pulsed electron beam,” Materials Technology, vol. 27, no. 4, pp. 300–303, 2012. View at Publisher · View at Google Scholar · View at Scopus
  19. J. Cheol Oh, D.-K. Choo, and S. Lee, “Microstructural modification and hardness improvement of titanium-base surface-alloyed materials fabricated by high-energy electron beam irradiation,” Surface and Coatings Technology, vol. 127, no. 1, pp. 76–85, 2000. View at Publisher · View at Google Scholar · View at Scopus
  20. Z. Zhong and S. J. Clouser, “Nickel-tungsten alloy brush plating for engineering applications,” Surface and Coatings Technology, vol. 240, pp. 380–386, 2014. View at Publisher · View at Google Scholar · View at Scopus