Tritium Breeding Performance Analysis of HCLL Blanket Fusion Reactor Employing Vanadium Alloy (V-5Cr-5Ti) as First Wall Material
Table 1
Atomic densities of blanket material in each zone.
| Zona | Materials | Atomic weight (gr/cm3) | Nuclide | Percentage of components (%) | Nuclei density(atom/barn.cm) |
| Coating layer | Be + W | 10.565 | Be | 50 | 6.178984E − 02 | W | 50 | 3.157400E − 02 |
| Structure | Eurofer97 | 7.909 | B | 0.001 | 1.681813E − 06 | C | 0.105 | 1.589460E − 04 | N | 0.018 | 2.335812E − 05 | O | 0.01 | 1.136275E − 05 | Al | 0.008 | 5.390778E − 06 | Si | 0.006 | 3.883318E − 06 | P | 0.004 | 2.348130E − 06 | S | 0.003 | 1.700692E − 06 | Ti | 0.008 | 3.038295E − 06 | V | 0.2 | 7.137966E − 05 | Cr | 9 | 3.075477E − 03 | Mn | 0.42 | 1.389838E − 04 | Fe | 88.98 | 2.896494E − 02 | Co | 0.005 | 1.542542E − 06 | Ni | 0.005 | 1.548865E − 06 | Cu | 0.005 | 1.430401E − 06 | Nb | 0.001 | 1.956775E − 07 | Mo | 0.001 | 1.894787E − 07 | Ta | 0.07 | 7.062309E − 06 | W | 1.1 | 1.088054E − 04 | SS316 | 8.00 | C | 0.03 | 1.202998E − 04 | N | 0.1 | 3.437545E − 04 | Si | 1 | 1.714489E − 03 | P | 0.045 | 6.997740E − 05 | S | 0.015 | 2.252572E − 05 | Cr | 17.5 | 1.620769E − 02 | Mn | 2 | 1.753185E − 03 | Fe | 64.81 | 5.588630E − 02 | Ni | 12 | 9.847091E − 03 | Mo | 2.5 | 1.254826E − 03 |
| FW | Seen in Table 2 | | | | | Coolant | Helium | 0.125 | He | 100 | 1.879840E − 02 |
| Breeder | LiPb | 10.52 | Li-6 | | 1.177322E − 02 | Li-7 | 17 | 1.433417E − 01 | Pb | 83 | 2.536968E − 02 |
| Shielding/reflector | BeO 50% + graphite 50% | 2.5215 | Be-9 | 257 | 3.634600E − 02 | O-16 | 25 | 3.634300E − 02 | C | 50 | 5.070100E − 02 |
| Magnetic coil | Nb3Sn (toroidal) | 8.69 | Nb | 15 | 8.445883E − 03 | Sn | 85 | 3.746144E − 02 | NbTi (poloidal) | 5.7 | Nb | 53 | 2.984212E − 02 | Ti | 47 | 5.136304E − 02 |
|
|