Tritium Breeding Performance Analysis of HCLL Blanket Fusion Reactor Employing Vanadium Alloy (V-5Cr-5Ti) as First Wall Material
Table 3
Atomic densities of candidate materials used in the first wall to increase the neutronic performances in blanket HCLL module.
| Nucleus | Nuclei density (atom/barn.cm) | VC | TiC | V-5Cr-5Ti | HT-9 | C | SiC | W-CuCrZr |
| V | 5.518E − 02 | | 6.573E − 02 | 2.309E − 04 | | | | C | 5.518E − 02 | 4.956E − 02 | 3.581E − 03 | 7.835E − 04 | 1.128E – 01 | 1.609E − 01 | | Ti | | 4.956E − 02 | 3.890E − 03 | | | | | Cr | | | 5.272E − 05 | 1.086E − 02 | | | 6.182E − 04 | N | | | 1.382E − 04 | | | | | O | | | 5.354E − 05 | | | | | Ni | | | | 4.914E − 04 | | | | Mn | | | | 5.138E − 04 | | | | Fe | | | | 7.122E − 02 | | | | Mo | | | | 4.903E − 04 | | | | W | | | | 6.700E − 04 | | | 3.154E − 02 | Si | | | | 6.700E − 04 | | 6.879E − 02 | | Cu | | | | | | | 4.156E − 02 | Zr | | | | | | | 5.888E − 05 | Total | 1.104E − 01 | 9.913E − 02 | 7.345-02 | 8.593E − 02 | 1.128E – 01 | 2.297E − 01 | 6.315E − 02 |
|
|