Influence of the Wave Form on the Material Response Delay

Table 2

Monotonic and cyclic mechanical properties of the studied material.

		42CrMo4
Tensile strength	Ru (MPa)	1100
Yield strength	Rp0.2%, (MPa)	980
Elongation	𝐴 (%)	16
Young’s modulus	𝐸 (GPa)	206
Cyclic yield strength	Rp0.2%, cyclic (MPa)	640
Strength coefficient	𝐾^′ (MPa)	1420
Strain hardening exponent	𝑛^′	0.12
Fatigue strength coefficient	𝜎𝑓^′ (MPa)	1154
Fatigue strength exponent	𝑏	−0.061
Fatigue ductility coefficient	𝜀𝑓^′	0.18
Fatigue ductility exponent	𝑐	−0.53