The Pore Collapse “Hot-Spots” Model Coupled with Brittle Damage for Solid Explosives
Table 1
Material parameters for PBX-9404.
| Material parameter | value |
| Initial density, (g/cm3) | 1.84 | Yield strength, (GPa) | 0.2 | Shear modulus, (GPa) | 4.54 | Viscosity, (GPa*s) | 0.1 | Initial temperature, (K) | 300 | Specific heat, (GPa*cm3/g/K) | | Frequency factor, (s−1) | | Activation energy, (GPa*cm3/mole) | 220.5 | Initial inner pore radius, (m) | 10.0 | Initial external pore radius, (m) | 46.416 | Initial crack radius, (m) | 10.0 | Fracture toughness, (GPa*) | | Terminal speed for crack growth, (cm/s) | | material constant, | 10 |
|
|