Research Article
Experimental Investigation of Ultrasonic Vibration Assisted Turning of 304 Austenitic Stainless Steel
Table 5
Surface roughness in UAT and CT used for experimental results.
| Number | Process parameters | Surface roughness | (mm/rev) | (mm) | (m/min) | (µm) | UAT | CT () | (µm) | (µm) | (µm) | (µm) |
| 1 | 0.08 | 0.1 | 22 | 15 | 1.72 | 2.17 | 1.83 | 2.24 | 2 | 0.08 | 0.1 | 22 | 23 | 1.44 | 1.80 | 1.83 | 2.24 | 3 | 0.08 | 0.1 | 22 | 30 | 1.61 | 2.01 | 1.83 | 2.24 | 4 | 0.08 | 0.1 | 21 | 23 | 1.34 | 1.66 | 1.56 | 1.88 | 5 | 0.1 | 0.1 | 21 | 23 | 1.54 | 1.96 | 1.65 | 2.02 | 6 | 0.15 | 0.1 | 21 | 23 | 1.69 | 2.11 | 2.02 | 2.51 | 7 | 0.2 | 0.1 | 21 | 23 | 1.71 | 2.13 | 1.89 | 2.32 | 8 | 0.08 | 0.05 | 21 | 23 | 1.31 | 1.63 | 1.51 | 1.83 | 9 | 0.08 | 0.1 | 21 | 23 | 1.34 | 1.66 | 1.56 | 1.88 | 10 | 0.08 | 0.15 | 21 | 23 | 1.49 | 1.86 | 1.81 | 2.30 | 11 | 0.08 | 0.2 | 21 | 23 | 1.60 | 2.01 | 1.81 | 2.24 | 12 | 0.08 | 0.1 | 18 | 23 | 2.22 | 2.70 | 1.47 | 1.87 | 13 | 0.08 | 0.1 | 21 | 23 | 1.34 | 1.66 | 1.56 | 1.88 | 14 | 0.08 | 0.1 | 22 | 23 | 1.44 | 1.80 | 1.83 | 2.24 | 15 | 0.08 | 0.1 | 23 | 23 | 1.68 | 2.12 | 1.77 | 2.19 | 16 | 0.1 | 0.1 | 18 | 23 | 2.63 | 3.22 | — | — | 17 | 0.1 | 0.1 | 21 | 23 | 1.60 | 2.01 | — | — | 18 | 0.1 | 0.1 | 23 | 23 | 1.46 | 1.83 | — | — | 19 | 0.1 | 0.1 | 25 | 23 | 1.40 | 1.73 | — | — | 20 | 0.1 | 0.1 | 28 | 23 | 1.60 | 2.01 | — | — | 21 | 0.1 | 0.1 | 33 | 23 | 1.63 | 2.04 | — | — | 22 | 0.1 | 0.1 | 42 | 23 | 1.80 | 2.27 | — | — | 23 | 0.1 | 0.1 | 47 | 23 | 1.85 | 2.34 | — | — | 24 | 0.1 | 0.1 | 22 | 15 | 1.73 | 2.16 | — | — | 25 | 0.1 | 0.1 | 25 | 15 | 1.37 | 1.72 | — | — | 26 | 0.1 | 0.1 | 28 | 15 | 1.64 | 2.04 | — | — | 27 | 0.1 | 0.1 | 33 | 15 | 1.67 | 2.09 | — | — | 28 | 0.1 | 0.1 | 42 | 15 | 1.86 | 2.36 | — | — | 29 | 0.1 | 0.1 | 47 | 15 | 1.97 | 2.51 | — | — |
|
|