Fabrication and Characterization of Natural Rubber-Based Magnetorheological Elastomers at Large Strain for Base Isolators
Table 7
MR effect of MRE with carbon black and naphthenic oil (0.5hz).
| Sample | C20N20 | C40N20 | C20N40 | C40N40 | C60N40 | Magnetic flux density (T) | 0 / 0.94 | 0 / 0.94 | 0 / 0.94 | 0 / 0.94 | 0 / 0.94 |
| Strain (%) | 25 | | | | | | Shear modulus (MPa) | 0.80 / 1.45 | 0.76 / 1.32 | 0.66 / 1.08 | 0.69 / 1.13 | 0.67 / 1.53 | MR effect (%) | 80.2 | 72.5 | 64.0 | 64.3 | 127.4 | 50 | | | | | | Shear modulus (MPa) | 0.58 / 1.00 | 0.58 / 0.97 | 0.45 / 0.72 | 0.47 / 0.79 | 0.52 / 1.07 | MR effect (%) | 73.1 | 67.9 | 58.2 | 67.9 | 106.9 | 75 | | | | | | Shear modulus (MPa) | 0.49 / 0.75 | 0.50 / 0.76 | 0.39 / 0.57 | 0.39 / 0.60 | 0.45 / 0.78 | MR effect (%) | 53.3 | 52.2 | 47.5 | 54.2 | 71.2 | 100 | | | | | | Shear modulus (MPa) | 0.42 / 0.56 | 0.47 / 0.60 | 0.35 / 0.44 | 0.38 / 0.48 | 0.45 / 0.60 | MR effect (%) | 33.2 | 26.9 | 27.1 | 26.6 | 33.5 |
|
|