Adaptive Damping of a Double-Beam Structure Based on Magnetorheological Elastomer

Table 1

Characterization of fabricated MRE samples.

Sample	Polymer matrix	Particles content	Density	Magnetic field during curing
1A	PU 70/30	11.5 vol.% Fe	1.82 g/cm^3	240 kA/m
1B	PU 70/30	33 vol.% Fe	3.28 g/cm^3	240 kA/m
2A	U1404	11.5 vol.% Fe	1.83 g/cm^3	240 kA/m
2B	U1404	33 vol.% Fe	3.30 g/cm^3	240 kA/m