Probabilistic Assessment of Damage from Same Shock Response Spectra due to Variations in Damping
Table 2
Fatigue damage data for various materials by Peng et al. [
8].
| 300CVM steel | Aluminum-2024-T42 | 30NiCrMoV12 steel | Normalized damage | Log(damage) | Normalized damage | Log(damage) | Normalized damage | Log(damage) |
| 0.76 | −0.121 | 0.85 | −0.072 | 0.58 | −0.238 | 0.82 | −0.087 | 0.78 | −0.106 | 0.78 | −0.107 | 1.03 | 0.012 | 0.69 | −0.164 | 0.83 | −0.083 | 1.22 | 0.086 | 0.64 | −0.192 | 0.80 | −0.095 | 1.03 | 0.011 | 0.66 | −0.178 | 0.74 | −0.133 | 1.61 | 0.207 | 0.70 | −0.153 | 1.04 | 0.019 | 1.11 | 0.045 | 0.84 | −0.074 | 0.91 | −0.041 | 1.30 | 0.114 | 0.74 | −0.133 | 0.69 | −0.162 | 1.10 | 0.043 | 0.88 | −0.057 | 0.86 | −0.068 | 0.46 | −0.341 | 1.18 | 0.072 | 1.17 | 0.069 | 0.51 | −0.296 | 1.24 | 0.095 | 1.27 | 0.105 | 0.77 | −0.112 | 1.25 | 0.098 | 1.54 | 0.187 | 1.05 | 0.023 | 1.39 | 0.144 | 1.07 | 0.028 | 1.45 | 0.160 | 1.40 | 0.147 | 1.28 | 0.106 | 0.90 | −0.046 | 1.29 | 0.109 | 1.41 | 0.150 | 0.76 | −0.120 | 1.26 | 0.100 | 1.08 | 0.035 | 1.13 | 0.055 | 1.20 | 0.080 | 0.95 | −0.022 | | | 1.16 | 0.064 | 0.85 | −0.072 | Standard deviation | 14.7% | | 12.3% | | 11.4% |
|
|