Research Article
A Generalized Method for Dispersion Analysis of Guided Waves in Multilayered Anisotropic Magneto-Electro-Elastic Structures
Table 1
Material properties used in the examples:
c (10
9 GPa),
e (C/m
2),
h (N/Am),
(10
−9 C
2/Nm
2),
(10
−6 Ns
2/C
2),
(Ns
2/C
2), and
(kg/m
3).
| | BaTiO3 | CoFe2O4 | Bimaterial | A | B |
| | 166 | 286 | 217.64 | 86.74 | | 77 | 173 | 125.3 | −8.25 | | 78 | 170.5 | 127.31 | 27.15 | | 0 | 0 | 1.34 | −3.66 | | 0 | 0 | −2.87 | 0 | | 0 | 0 | −1.43 | 0 | | 166 | 286 | 222.02 | 129.77 | | 78 | 170.5 | 125.44 | −7.42 | | 0 | 0 | −2.72 | 5.7 | | 0 | 0 | 0.49 | 0 | | 0 | 0 | −2.35 | 0 | | 162 | 269.5 | 216.25 | 102.83 | | 0 | 0 | −1.13 | 9.92 | | 0 | 0 | −1.95 | 0 | | 0 | 0 | 1.62 | 0 | | 43 | 45.3 | 47.31 | 38.81 | | 0 | 0 | 0.54 | 0 | | 0 | 0 | −1.68 | 0 | | 43 | 45.3 | 47.94 | 68.81 | | 0 | 0 | 0.09 | 2.53 | | 44.5 | 56.5 | 47.8 | 29.01 | | 0 | 0 | 5.73 | 0.171 | | 0 | 0 | −1.35 | −0.152 | | 0 | 0 | −1.38 | −0.019 | | 0 | 0 | −0.02 | 0.067 | | 11.6 | 0 | 4.07 | 0 | | 0 | 0 | 2.04 | 0 | | 0 | 0 | −0.79 | 0 | | 0 | 0 | 3.32 | 0 | | 0 | 0 | −0.8 | 0 | | 11.6 | 0 | 4.09 | 0 | | 0 | 0 | −0.02 | 0.108 | | 0 | 0 | 3.54 | −0.095 | | −4.4 | 0 | −1.58 | 0 | | −4.4 | 0 | −1.56 | 0 | | 18.6 | 0 | 6.61 | 0 | | 0 | 0 | 2.03 | 0 | | 0 | 0 | 3.52 | −0.076 | | 0 | 0 | −0.02 | 0.067 | | 0 | 0 | 401.95 | 0 | | 0 | 0 | 140.19 | 0 | | 0 | 0 | 27.62 | 0 | | 0 | 0 | −75.05 | 0 | | 0 | 550 | 64.47 | 550 | | 0 | 0 | 32.24 | 0 | | 0 | 0 | 37.61 | 0 | | 0 | 0 | 275.39 | 0 | | 0 | 0 | 15.95 | 0 | | 0 | 550 | 151.13 | 550 | | 0 | 0 | −75 | 0 | | 0 | 0 | 130.88 | 0 | | 0 | 580.3 | 75.22 | 580.3 | | 0 | 580.3 | 161.87 | 580.3 | | 0 | 699.7 | 420.8 | 699.7 | | 0 | 0 | 10.57 | 0 | | 0 | 0 | 18.31 | 0 | | 0 | 0 | −75.05 | 0 | | 11.2 | 0.08 | 6 | 0.392 | | 0 | 0 | 0 | 0 | | 0 | 0 | 0.35 | 0 | | 11.2 | 0.08 | 5.64 | 0.398 | | 0 | 0 | 0 | 0.86 | | 12.6 | 0.093 | 6 | 0.404 | | 5 | 590 | 190.25 | 5 | | 0 | 0 | 0 | 0 | | 0 | 0 | −106.8 | 0 | | 5 | 590 | 297 | 5 | | 0 | 0 | 0 | 0 | | 10 | 157 | 190.25 | 10 | | 0 | 0 | 0.05 | 0 | | 0 | 0 | 0 | 0 | | 0 | 0 | 0 | 0 | | 0 | 0 | 0.05 | 0 | | 0 | 0 | 0 | 0 | | 0 | 0 | 0.03 | 0 | | 5800 | 5300 | 5550 | 4900 |
|
|