The preferred orientation of MnS inclusions in hot-rolled steel was studied by electron diffraction.
Specimens of resulfurized steel were examined after casting and after hot rolling to true strains of
0.5, 1.0 and 1.5. After rolling, the orientations of the inclusions tended toward an ideal