Parametric Appraisal of Process Parameters for Adhesion of Plasma Sprayed Nanostructured YSZ Coatings Using Taguchi Experimental Design
Table 3
L16 Orthogonal array design with output and S/N ratio.
| Test run | Torch input power (kW) | Particle temperature (°C) | Particle velocity (m/sec) | Substrate roughness (μm) | SOD (mm) | Adhesion strength (MPa) | S/N ratio |
| 1 | 30 | 2500 | 200 | 4 | 75 | 30.39 | 29.6546 | 2 | 30 | 2600 | 225 | 5 | 100 | 36.67 | 31.2862 | 3 | 30 | 2700 | 250 | 6 | 125 | 32.89 | 30.3413 | 4 | 30 | 2800 | 275 | 7 | 150 | 29.45 | 29.3817 | 5 | 35 | 2500 | 275 | 6 | 100 | 28.72 | 29.1637 | 6 | 35 | 2600 | 250 | 7 | 75 | 38.75 | 31.7654 | 7 | 35 | 2700 | 225 | 4 | 150 | 35.29 | 30.9530 | 8 | 35 | 2800 | 200 | 5 | 125 | 37.12 | 31.3922 | 9 | 40 | 2500 | 225 | 7 | 125 | 38.71 | 31.7565 | 10 | 40 | 2600 | 200 | 6 | 150 | 39.37 | 31.9033 | 11 | 40 | 2700 | 275 | 5 | 75 | 33.90 | 30.6040 | 12 | 40 | 2800 | 250 | 4 | 100 | 31.59 | 29.9910 | 13 | 45 | 2500 | 250 | 5 | 150 | 34.79 | 30.8291 | 14 | 45 | 2600 | 275 | 4 | 125 | 30.43 | 29.6660 | 15 | 45 | 2700 | 200 | 7 | 100 | 38.49 | 31.7070 | 16 | 45 | 2800 | 225 | 6 | 75 | 29.50 | 29.3964 |
|
|