Semisolid Metal Processing Techniques for Nondendritic Feedstock Production
Figure 35
Microstructures of Zn-22Al (a) as-cast, (b) after DPRM at 438°C for 60 min in an as-cast sample, and (c) after solution treatment for 3 hours then subjected to DPRM at 438°C for 60 min [69].