Impact Strength and Flexural Properties Enhancement of Methacrylate Silane Treated Oil Palm Mesocarp Fiber Reinforced Biodegradable Hybrid Composites
Table 2
Tensile properties of unmodified and silane treated OPMF hybrid composites.
| Sample | Tensile strength (MPa) | Elongation at break (mm) | Tensile modulus (MPa) |
| PLA85/PCL15 | 45.94 ± 1.75 | 1.68 ± 0.30 | 902.92 ± 50.69 | Unmodified OPMF hybrid composites | | | | PLA85/PCL15/1 wt% clay/10 wt% OPMF | 36.32 ± 1.22 | 0.74 ± 0.02 | 685.80 ± 71.32 | PLA85/PCL15/1 wt% clay/20 wt% OPMF | 32.32 ± 0.55 | 0.64 ± 0.10 | 661.17 ± 46.36 | PLA85/PCL15/1 wt% clay/30 wt% OPMF | 29.46 ± 1.58 | 0.61 ± 0.02 | 577.18 ± 27.04 | Silane treated OPMF hybrid composites | | | | PLA85/PCL15/1 wt% clay/10 wt% OPMF | 40.45 ± 0.94 | 0.95 ± 0.01 | 865.50 ± 50.24 | PLA85/PCL15/1 wt% clay/20 wt% OPMF | 33.18 ± 0.86 | 0.63 ± 0.06 | 842.55 ± 45.63 | PLA85/PCL15/1 wt% clay/30 wt% OPMF | 29.35 ± 0.53 | 0.62 ± 0.02 | 767.70 ± 56.50 |
|
|