The Modification of Polyurethane Foams Using New Boroorganic Polyols (II) Polyurethane Foams from Boron-Modified Hydroxypropyl Urea Derivatives
Table 5
Dimensional stability of polyurethane foams.
| Foam type | Dimensional stability (linear %) in 150°C | Length | Width | Thickness | After 20 h | After 40 h | After 20 h | After 40 h | After 20 h | After 40 h |
| FA1 | 1.96 ± 0.03 | 1.96 ± 0.05 | 2.86 ± 0.09 | 2.86 ± 0.09 | 2.68 ± 0.23 | 2.65 ± 0.23 | FA2 | 0.84 ± 0.03 | 0.84 ± 0.04 | 1.11 ± 0.03 | 1.11 ± 0.03 | 0.99 ± 0.07 | 0.99 ± 0.09 | FA3 | 1.32 ± 0.11 | 1.76 ± 0.13 | 0.13 ± 0.03 | 1.39 ± 0.50 | 0.45 ± 0.03 | 0.90 ± 0.04 | FB1 | 0.64 ± 0.05 | 0.64 ± 0.06 | 0.00 ± 0.00 | 0.68 ± 0.02 | 0.00 ± 0.00 | 0.00 ± 0.00 | FB2 | 0.15 ± 0.02 | 0.75 ± 0.05 | 0.52 ± 0.02 | 2.09 ± 0.06 | 0.00 ± 0.00 | 1.06 ± 0.11 | FB3 | 1.91 ± 0.12 | 2.23 ± 0.67 | 0.54 ± 0.04 | 0.45 ± 0.02 | 0.48 ± 0.06 | 0.68 ± 0.09 | FC1 | 18.40 ± 1.50 | 16.89 ± 1.28 | 16.11 ± 1.93 | 15.98 ± 1.79 | 3.91 ± 0.42 | 8.59 ± 0.76 | FC2 | 7.87 ± 0.26 | 9.55 ± 0.23 | 5.51 ± 0.43 | 8.27 ± 0.55 | 6.25 ± 0.29 | 10.42 ± 0.72 | FC3 | 8.28 ± 0.82 | 9.08 ± 1.01 | 14.58 ± 1.38 | 15.23 ± 1.54 | 15.94 ± 1.60 | 19.81 ± 2.02 |
|
|