| S. no. | Sample | % ZnO NPS | Current , amperes | Resistance (R), OHM | Sample thickness , cm | , /cm |
|
| 1 | PANI | — | 8 * 10−12 | 2.5 * 1012 | 0.088 | 4.5 * 10−14 |
| 2 | PANI/ZnO (in absence of surfactant) | 20 | 9 * 10−12 | 2.22 * 1012 | 0.093 | 5.3 * 10−14 |
| 3 | PANI/ZnO (in absence of surfactant) | 40 | 18 * 10−12 | 1.11 * 1012 | 0.147 | 1.6 * 10−13 |
| 4 | PANI/ZnO (in absence of surfactant) | 60 | 15 * 10−12 | 1.33 * 1012 | 0.191 | 1.82 * 10−13 |
| 5 | PANI/ZnO (in absence of surfactant) | 80 | 7 * 10−12 | 2.85 * 1012 | 0.004 | 1.79 * 10−15 |
| 6 | PANI/ZnO (in presence of surfactant, SLS, under microwave) | 20 | 25 * 10−12 | 0.80 * 1012 | 0.195 | 3.1 * 10−13 |
| 7 | PANI/ZnO (in presence of surfactant, SLS, under microwave) | 40 | 21 * 10−12 | 0.95 * 1012 | 0.109 | 1.46 * 10−13 |
| 8 | PANI/ZnO (in presence of surfactant, SLS, under microwave) | 60 | 35.2 * 10−12 | 0.57 * 1012 | 0.19 | 4.2 * 10−13 |
| 9 | PANI/ZnO (in presence of surfactant, SLS, under microwave) | 80 | 5 * 10−12 | 4.0 * 1012 | 0.143 | 4.55 * 10−14 |
| 10 | PANI/ZnO (in presence of surfactant, SLS, under pressure) | 20 | 11 * 10−12 | 1.82 * 1012 | 0.129 | 9.1 * 10−14 |
| 11 | PANI/ZnO (in presence of surfactant, SLS, under pressure) | 40 | 10 * 10−12 | 2.0 * 1012 | 0.181 | 1.15 * 10−13 |
| 12 | PANI/ZnO (in presence of surfactant, SLS, under pressure) | 60 | 6 * 10−12 | 3.33 * 1012 | 0.180 | 6.9 * 10−14 |
| 13 | PANI/ZnO (in presence of surfactant, SLS, under pressure) | 80 | 4 * 10−12 | 5.0 * 1012 | 0.150 | 3.8 * 10−14 |
| 14 | PANI/ZnO (in presence of surfactant, SLS, under vacuum) | 20 | 16 * 10−12 | 1.25 * 1012 | 0.115 | 1.17 * 10−13 |
| 15 | PANI/ZnO (in presence of surfactant, SLS, under vacuum) | 40 | 11 * 10−12 | 1.81 * 1012 | 0.199 | 1.40 * 10−13 |
| 16 | PANI/ZnO (in presence of surfactant, SLS, under vacuum) | 60 | 24 * 10−12 | 0.833 * 1012 | 0.194 | 2.9 * 10−13 |
| 17 | PANI/ZnO (in presence of surfactant, SLS, under vacuum) | 80 | 18 * 10−12 | 1.11 * 1012 | 0.114 | 1.3 * 10−13 |
| 18 | PANI/ZnO (in presence of surfactant, SLS, at room temperature) | 20 | 9 * 10−12 | 2.22 * 1012 | 0.150 | 8.6 * 10−14 |
| 19 | PANI/ZnO (in presence of surfactant, SLS, at room temperature) | 40 | 13 * 10−12 | 1.53 * 1012 | 0.249 | 2.07 * 10−13 |
| 20 | PANI/ZnO (in presence of surfactant, SLS, at room temperature) | 60 | 9 * 10−12 | 2.22 * 1012 | 0.10 | 5.7 * 10−14 |
| 21 | PANI/ZnO (in presence of surfactant, SLS, at room temperature) | 80 | 8 * 10−12 | 2.5 * 1012 | 0.11 | 5.6 * 10−14 |
|