The Process of Nanostructuring of Metal (Iron) Matrix in Composite Materials for Directional Control of the Mechanical Properties

Table 4

The study of mechanical properties of the synthesized composite materials based on iron with dispersed phase of TiC.

Sample	Composition	Tensile strength, 𝜎𝐵, MPa
Obtained samples
MN-ALD method
1	100% Fe	183
2	95,5% Fe + 1,5% TiC	800
3	97% Fe + 3% TiC	1130
4	90,5% Fe + 9,5% TiC	1370
5	84,5% Fe + 15,5% TiC	1460
CVD method
6	69,5% Fe + 30,5% TiC	890
7	61,5% Fe + 38,5% TiC	900
Literature data [37]
7	Steel AS 14CGN	1120
8	Steel 50CG	1300
9	Steel 12C2N4A	1130
10	High-strength steel	1500

∗The residual porosity of the synthesized samples was 5–6 %.