Electrochemical Characterization of Nanoporous Nickel Oxide Thin Films Spray-Deposited onto Indium-Doped Tin Oxide for Solar Conversion Scopes

<div>Scan rate dependence of the cathodic peak positioned at around 3.1 V versus Li<sup>+</sup>/Li for the sample of CS NiO (<svg height="9.49473pt" id="M76" style="vertical-align:-0.2063999pt" version="1.1" viewbox="-0.0498162 -9.28833 34.035 9.49473" width="34.035pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M238 681C243 705 239 712 230 712C217 712 156 682 75 674L70 648H105C148 648 153 641 144 598L39 110C18 11 35 -12 55 -12C90 -12 166 36 221 103L205 125C174 93 130 65 118 65C112 65 108 68 114 96L238 681Z" id="g113-109"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="269" vert-adv-y="269"></glyph.data></g><g transform="matrix(.013,0,0,-0.013,7.13,0)"><path d="M535 323V373H52V323H535ZM535 138V188H52V138H535Z" id="g117-34"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="587" vert-adv-y="587"></glyph.data></g><g transform="matrix(.013,0,0,-0.013,18.393,0)"><path d="M241 635C89 635 35 457 35 312C35 153 89 -12 240 -12C390 -12 443 166 443 312C443 466 390 635 241 635ZM238 602C329 602 354 454 354 312C354 172 330 22 240 22C152 22 124 173 124 313S148 602 238 602Z" id="g113-49"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="480" vert-adv-y="480"></glyph.data></g><g transform="matrix(.013,0,0,-0.013,24.633,0)"><path d="M113 -12C146 -12 170 11 170 46C170 78 146 103 114 103S58 78 58 46C58 11 82 -12 113 -12Z" id="g113-47"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="228" vert-adv-y="228"></glyph.data></g><g transform="matrix(.013,0,0,-0.013,27.597,0)"><path d="M285 378C315 398 338 416 353 432C373 451 384 474 384 503C384 579 325 635 236 635H235C182 635 136 610 108 579L65 516L85 496C110 533 150 575 205 575C258 575 300 543 300 481C300 407 232 369 141 339L147 310C163 315 188 321 211 321C268 321 338 284 338 192C338 94 288 40 217 40C160 40 119 68 93 91C85 98 77 97 69 91C60 84 47 71 46 58C44 46 48 35 62 22C75 10 116 -12 162 -12C234 -12 424 62 424 224C424 297 373 359 285 376V378Z" id="g113-52"></path><glyph.data ascent="3473" descent="-2876" horiz-adv-x="480" vert-adv-y="480"></glyph.data></g></svg> <i>μ</i>m) spray-deposited onto ITO. Cell configuration and electrolyte composition as in Figure <a href="../fig1/">1</a>. Data extracted from Figure <a href="../fig7/">7</a>.</div>

Advances in Condensed Matter Physics

fig11

Figure 11

Figure 11: Electrochemical Characterization of Nanoporous Nickel Oxide Thin Films Spray-Deposited onto Indium-Doped Tin Oxide for Solar Conversion Scopes 

Figure 11 | Electrochemical Characterization of Nanoporous Nickel Oxide Thin Films Spray-Deposited onto Indium-Doped Tin Oxide for Solar Conversion Scopes 